Base oil of chain lubs

1) Unique cleanness of PAG product, their breakdown products could dissolved in lubricant and wouldnt produce fatlute, carbon deposit film and soot.

(2) High boiling point and flash point could be used in high temperature safely, Good lubricity and synergistic interaction with antioxygen, recommend using in 200℃ such as textile printing and dyeing industry.

(3)Unique design and process to avoid sinkhole on surface of film ,used at 240℃ to meet the need of automobile industry.

4Low or Non toxicity of PAG could be used in chain of food contract machine. Low viscosity PAG is biodegradable.

products

Viscosity

40mm2/s

Viscosity

100mm2/s

VI

Acid value

mgKOH/g


Flash point

Pour point

Water content


%

SDT-05A

220

34

190

0.05

220

-30

0.1

SDT-055A

330

55

220

0.05

220

-30

0.1

SDN-06A

460

70

230

0.1

230

-30

0.1

SDM-150W

150

29

210

0.05

220

-40

0.1

SDD-06D

320

58

240

0.05

240

-36

0.1

SDD-07D

460

80

250

0.05

240

-35

0.1

SDD-08D

1000

180

280

0.05

240

-31

0.1


Use Dipe polyol ester and polycarboxylic acid ester as base oil for high chain transmittal could be used in 250300℃high temperature.

Excellent oxidation stability at high temperature ,little coking and evaporation loss.

Products

Acid Value

Viscosity

Viscosit

VI

Pour point

Flash point

Mgkoh/g ≤

40mm2/s

100 mm2/s

SDYZ-11

0.05

30

5.8

144

-4

290

POE-100

0.05

100

11

100

-38

260

POE-170-A

0.05

170

15.5

90

-28

270

POE-380

0.05

380

25.88

90

-18

310

SDBZ-1

0.05

115

11.3

80

-50

260

SDBZ-2

0.05

310

20.7

75

-27

270

SDPZ-2

0.05

50

8

110

-40

270

SDPZ-3

0.05

320

26.8

110

-30

275

SDJZ-2

0.05

88

11.8

120

-40

290

SZ-2021B

0.1

47000

2000

250

6

325